  • Lithium ion Battery Pouch Case Made by Aluminum Laminated Film
Lithium ion Battery Pouch Case Made by Aluminum Laminated Film

Lithium ion Battery Pouch Case Made by Aluminum Laminated Film

  • Model: Pouch Cell Case
  • Material: Aluminum Laminated Film
  • Thickness: 113um
  • Size: Customized
  • Product description: Lithium ion Battery Pouch Case Made by Aluminum Laminated Film
  • INQUIRY

Aluminum laminated film 113micron thickness lithium ion pouch battery packing case/cup

 

The sizes can be customized according to the requirement.


There is three kind of thickness for your choice: 88um, 113um, 153um. The 113um is most popular.

 

Aluminum Laminated Film Specification

 

 

 

 

 

Consist

D-EL40H

ON25

DL4

AL40

Improved PPa15

Improved PP30

Acid modified resin combination, waterproof and acid attacks

 (Thickness 113µm)

Thickness

µm

Designed

113

Steam Barrier Property

60°C90%RH 336H

PPm

Sealing Pressure 1.0MPa

50↓

Initial strength of laminated layers(AL/PPa)

N/15mm

 

11~12

Initial sealing strength

N/15mm

Sealing Pressure 0.5MPa

70~80

190°C 3seconds

Sealing Pressure 1.0MPa

85↑

The electrolyte resistance(Test for sealing into film strength)

N/15mm

 

4.0↑

60°C 14days

Electrolyte resistance(Test for sealing into film strength)

N/15mm

Sealing Pressure 0.5MPa

40~50

60°C 14days

Sealing Pressure 1.0MPa

50~60

Sealing strength for electrolyte

N/15mm

Sealing face pressure 0.5MPa

80~90

190°C 3seconds

Sealing face pressure 1.0MPa

80~90

Punch forming depth

mm

Control drape pressure 0.17MPa(Size:80*120mm)

5.0↑

 